Abstract
A series of novel copolyesters based on polyethylene terephthalate (PET) and 4′-hydroxy-biphenyl-4-carboxylic acid (HBCA) was obtained by melt polycondensation of bis(2-hydroxyethyl) terephthalate and 4′-acetoxybiphenyl-4-carboxylic acid (ABCA) as co-monomers with Sb2O3 as a catalyst. Using this synthetic procedure, a set of copolymers containing 20–80 mol% of HBCA units was prepared. According to NMR spectroscopy, the copolymers were of random composition. Copolyesters comprising 60–80 mol% of HBCA possessed increased heat resistance and formed nematic melts at 270 °C and higher. The liquid crystal (LC) phase formation was accompanied by transition to non-Newtonian characteristics of the melt flow, as well as an equalization of storage and loss moduli values. According to XRD and polarizing microscopy, the LC glassy phase of the copolyesters coexists with crystalline regions of poly-(4′-hydroxy-4-biphenylcarboxylate), non-melting up to 400 °C and above. The mechanical characteristics of these LC copolyesters showed similar or better values than those of well-known LC polymers. These novel copolyesters can be useful in obtaining heat-resistant materials with an ordered structure and, as a consequence, improved performance.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.