Abstract
A (Li, Cu)-co-doped cathode material Li(Li0.05Cu0.05Mn1.90)O4 was prepared by a flameless combustion synthesis at 500 °C for 3 h and then two-stage calcination at 700 °C for 6 h. Physical and electrochemical performances were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscope (TEM), galvanostatic charge–discharge cycling test, cyclic voltammogram (CV) and electrochemical impedance spectroscopy (EIS) to investigate the influence of Li and Cu substitution on the lithium ion batteries. Li(Li0.05Cu0.05Mn1.90)O4 not only exhibited the initial discharge capacity of 106.9 mAh g−1 with a high retention of 89.2% after 500 cycles at 1.0 C but also retained 63.5% capacity after 1500 cycles at 5.0 C. Besides, a good rate capability at different current densities from 0.5 C to 5.0 C can be acquired. The (Li, Cu)-co-doped sample had excellent cycling stability in comparison with the LiMn2O4 cathode.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.