Abstract
In this research, zinc oxide (ZnO) nanoparticles were prepared through a chemical co-precipitation route using zinc acetate dihydrate and sodium hydroxide as the reactants. To study the variation in the properties of the nanoparticles, namely its phase, shape and size, the reaction temperature and stirring rate were varied during the synthesis process. From the X-ray diffraction profiles, the as-synthesised samples were confirmed to be ZnO. Spherical and hexagonal-shaped particles were obtained when the temperature and stirring rate were varied. A rise in the synthesis temperature from 30 to 70°C caused insignificant changes to the average diameter of the particles, although their shape was altered from spherical to hexagonal. When the stirring rate was increased, the average diameter of the particles decreased. The average diameter of the sample calcined at 600°C for 1 hour recorded a slight increase while its X-ray diffraction profile depicted narrower peaks with higher intensity, indicating formation of a more stable phase of ZnO. Further study is needed to elucidate the effects of the particle shape and sizes on the thermoelectric transport properties.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.