Abstract
The effect of sigma-phase precipitation on plastic anisotropy of the equiatomic CoCrFeMnNi high-entropy alloy was investigated. Annealing at 700 °C after cold-rolling leads to the formation of the Cr-rich σ phase with a fraction of 2.7%. It is experimentally found that the planar anisotropy (∆r = -0.16) of the CoCrFeMnNi alloy annealed at 700 °C is two times lower than that of the alloy annealed at 800 °C (∆r = -0.35). This observation was further supported by measuring the earing profile of cup specimens after the deep drawing process. The plastic strain ratio, normal anisotropy, and planar anisotropy were also predicted using the visco-plastic self-consistent model. The results indirectly indicated that the reduction of plastic anisotropy in alloy annealed at 700 °C can be attributed to the formation of the σ phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.