Study on the sintered characteristics and properties of nanostructured WC–15 wt% (Fe–Ni–Co) and WC–15 wt% Co hard metal alloys

Abstract

In this work, four different vacuum sintering temperatures (1250 °C, 1300 °C, 1350 °C and 1400 °C) were studied to determine the optimal process parameters of nano WC–15 wt% (Fe–Ni–Co) and WC–15 wt% Co sintered hard metal alloys. Experimental results showed that the optimal sintering temperatures for nano WC–(Fe–Ni–Co) and WC–Co alloys were 1300 °C and 1350 °C for 1 h, respectively. The sintered nano WC–(Fe–Ni–Co) and WC–Co hard metal alloys showed a good contiguity of 0.44 and 0.42; hardness was enhanced to HRA 90.83 and 90.92; the transverse rupture strength (TRS) increased to 2567.97 and 2860.08 MPa; and KIC was 16.23 and 12.33 MPa√m, respectively. Although the nano WC–(Fe–Ni–Co) alloys possessed a slightly lower TRS value, they exhibited superior fracture toughness (KIC) and hardness similar to that of the nano WC–Co material. Significantly, nano WC–(Fe–Ni–Co) alloys could be sintered at a lower temperature and still retained their excellent mechanical properties.