Abstract
A ternary Fe–Cr–Ni alloy, akin to super martensitic stainless steels was prepared in vacuum induction furnace. The as cast ingot was solution treated at 1200°C for 25h and then hot forged and rolled to reduce into plate form. The hot rolled plate of martensitic microstructure was then cold rolled to 80% of thickness reduction. The phase transformation studies by X-ray diffraction analysis of hot and cold rolled specimens showed presence of retained austenite in air cooled as well as in water quenched state after annealing/austenising temperature of 1060°C. The reaustenisation behaviour of the cold rolled alloy in water quenched state was studied by high temperature X-ray diffraction analysis. It showed very stable martensitic phase and the completion of reaustenisation process were observed to occur at about 950°C. The recrystallisation behaviour of cold rolled material under isothermal and repeated annealing treatment was studied in detail by electron microscope. The tensile properties of the material were evaluated after various annealing treatments. The study revealed that by a suitable sequence of repetitive annealing process microstructure could be tailored to achieve tensile strength above 1GPa with good ductility in a super martensitic stainless steel.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.