Abstract
Pb(Zr0.52Ti0.48)O3 (PZT) thin films were crystallized on SrTiO3 (100) and MgO (100) substrates by a sol-gel process using nonhydrolyzed metal methoxyethoxide precursors, spin coating, and rapid thermal annealing. Solid phase epitaxial growth of PZT on SrTiO3 was observed directly from the amorphous phase even at 425 °C. The PZT had a single (001) orientation and rocking curve full width at half maximum (FWHM) less than 0.1°. High-temperature annealing of MgO substrates improved orientation of PZT thin films. Epitaxial crystallization of PZT with a single (001) orientation on the annealed MgO was observed at temperature above 550 °C after the formation of the pyrochlore phase.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.