Abstract
PurposeTo investigate the effect of the metallization and solder mask materials on the solder joint reliability of low temperature co‐fired ceramic (LTCC) modules.Design/methodology/approachThe fatigue performance of six LTCC/PCB assembly versions was investigated using temperature cycling tests in the −40‐125°C and 20‐80°C temperature ranges. In order to eliminate fatigue cracking in the LTCC module itself, large AgPt‐metallized solder (1 mm) lands with organic or co‐fired glaze solder masks, having 0.86‐0.89 mm openings, were used. The performance of these modules was compared to that of AgPd‐metallized modules with a similar solder land structure. The joint structures were analysed using resistance measurements, scanning acoustic microscopy, SEM/EDS investigation, and FEM simulations.FindingsThe results showed that failure distributions with Weibull shape factor (β) values from 8.4 to 14.2, and characteristic life time (θ) values between 860 and 1,165 cycles were achieved in AgPt assemblies in the −40‐125°C temperature range. The primary failure mechanism was solder joint cracking, whereas the AgPd‐metallized modules suffered from cracking in the ceramic. In the milder test conditions AgPd‐metallized modules showed better fatigue endurance than AgPt‐metallized modules.Originality/valueThis paper proves that the cracking in ceramic in the harsh test condition can be eliminated almost completely by using AgPt metallization instead of AgPd metallization in the present test module structure.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.