Abstract
We carried out in situ annealing of InP nanowires (NWs) in a metal-organic vapor phase epitaxial (MOVPE) growth reactor to control and reduce the tip size of InP NWs. InP NWs were grown by selective-area (SA) MOVPE on partially masked (111)A InP substrates, and annealing was successively applied in tertiarybutylphosphine (TBP) ambient. Initially, the InP NWs had a hexagonal cross-section with {112¯} facets vertical to the substrates; they became tapered, and the edges were rounded by annealing. By appropriately selecting the annealing temperature and initial NW diameter, the tip size of the NW was reduced and NWs with a tip size of 20 nm were successfully formed. Subsequently, a thin InAsP layer was grown on the annealed NWs and their photoluminescence was investigated at low temperatures. The characterization results indicated the formation of InAsP quantum dots (QDs) emitting in the telecom band. Our approach is useful for reducing the size of the NWs and for the controlled formation of InAsP QDs embedded in InP NWs in photonic devices compatible with telecom bands.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.