Size- and phase-dependent mechanical properties of ultrathin Si films on polyimide substrates

Abstract

Ultrathin Si films in the nanometer range are extensively used for electronic and optoelectronic devices. Their mechanical properties have a high impact on the durability of the devices during lifetime. Here, fragmentation and buckling of 8–103 nm thin amorphous and polycrystalline (poly-) Si films on polyimide substrates have been studied by in situ light microscopy, Raman spectroscopy and resistance measurements. Generally, a smaller film thickness and a compressive residual stress delays the fracture of the film. The fracture strength of poly-Si films is larger compared to that of amorphous Si films while the adhesion to the substrate is better for amorphous Si compared to poly-Si. The onset delamination as a function of film thickness differs for the two phases and is described by two different models. Thin-film models for fracture toughness (amorphous Si: K1C = 1.49 ± 0.22, poly-Si: K1C = 3.36 ± 1.37) are applied, discussed, and found to be consistent with literature values.