Abstract
Performance of aircraft in general, its systems and airframe materials, can be significantly reduced by environmental conditions in which the aircraft operates during the service life. Material performance of steel and aluminum alloys can be greatly degraded because of the environmental conditions (temperature, humidity, UV radiation, pollutants, etc.), which severely affect the integrity and safety of aircraft structure. Apart from the other severe environmental conditions, the effect of the corrosion on structural integrity is a critical issue for damage tolerance design and analysis and needs to be carefully investigated. The corrosion and corrosion fatigue failure process of an aircraft structure are directly concerned with many factors, such as load, material characteristics, and corrosive environment and so on. Attention in this paper is focused on the application of the Nondestructive Inspection (NDI) methods in the process of extension of service life of aircraft structures. The NDI methods were used as a part of service life extension program for the extension of the operation life of the G-4 Super Galeb aircraft structures that have been in service in air force for more than 25 years. The computation and experimental NDI methods and practice steps that diminish the negative effects of corrosion process were shown in this paper. Special attention in this paper is focused to the use of the NDI methods. These steps enable to extend the service life of aircraft structures beyond its designed service life with the accurate prediction of the further service reliability.
Highlights
TODAY many aging aircraft in air forces of many world’s countries have been in service beyond their airframe nominal designed service life [1,2,3,4]
The process of an aircraft aging, aging of its structure and equipment cannot be stopped but it could be rather diminished using several practical approaches, such as: - identification of critical points based on computation stress/strength analyses, components, and areas where the consequence of aging can cause a serious outcome, - visual control and analysis of the aging process at the oldest airplanes in service or equipment components, - analysis of the official maintenance procedures addressed to the aging problem, - improving of the protective maintenance methods in order to focus on aging in an early phase of its appearance
Understanding the influence of different factors on degradation of structure integrity is very important in order to manage corrosion occurrences on an aging aircraft
Summary
Performance of aircraft in general, its systems and airframe materials, can be significantly reduced by environmental conditions in which the aircraft operates during the service life. Material performance of steel and aluminum alloys can be greatly degraded because of the environmental conditions (temperature, humidity, UV radiation, pollutants, etc.), which severely affect the integrity and safety of aircraft structure. Apart from the other severe environmental conditions, the effect of the corrosion on structural integrity is a critical issue for damage tolerance design and analysis and needs to be carefully investigated. Attention in this paper is focused on the application of the Nondestructive Inspection (NDI) methods in the process of extension of service life of aircraft structures. Special attention in this paper is focused to the use of the NDI methods. These steps enable to extend the service life of aircraft structures beyond its designed service life with the accurate prediction of the further service reliability
Sign-in/Register to view highlights & summary Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call