Abstract
AlxZnyO thin films were obtained by reactive pulsed magnetron sputtering. A two-element Zn/Al planar target was used as source material prepared in the form of a Zn disc (100 mm diameter) with Al rings pressed into its surface. The sputtering processes were carried out in a mixture of argon and oxygen. The films were deposited with a discharge power of PE = 400 W, which corresponded to a power density on the target surface of approximately 5 W/cm2. The films were deposited on glass strip substrates, placed symmetrically over the target, making it possible to obtain films with different composition and thickness. The film sheet resistance was measured as a function of the distance from the target axis on both sides (front and back) of the substrate. The lowest measured resistivity was about 4 × 10−3 Ω·cm. Additionally, optical properties, surface topography, and elemental composition were determined in selected areas of the substrate.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.