Abstract
Vanadium pentoxide (V2O5) films with micro-nanostructure were fabricated by an electrodeposition method using an aqueous solution of NH4VO3. The surface morphology and structural properties of the V2O5 were investigated by SEM and XRD measurements. The results show that the annealing temperature strongly affects the surface morphology, crystal structure, and photoluminescence (PL) properties. The formation of α-V2O5 structure occurred when the sample was annealed at temperatures below 500 ℃. As the annealing temperature increases, some of the α-V2O5 structures were distorted and restructured to form a high-quality mix of α-β phase V2O5. This leads to great enhancement of the PL due to the presence of numerous defects on the surface of the V2O5 films. Moreover, the mixing of the α-β phase V2O5 leads to wide absorption and enhancement of the visible-light emission from V2O5 micro-nanostructure.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.