Abstract
Crystallographic characterization and the ferroelectric properties of 50 nm-thick sputter-deposited Al0.78Sc0.22N films deposited at room temperature (RT) and 400 °C are investigated. c-axis oriented growths were confirmed by x-ray diffraction patterns with rocking curve measurements for both samples. Al0.78Sc0.22N films were found to grow in the c-axis direction and showed poling-free ferroelectric properties, which are advantageous for practical memory and piezoelectric applications. Although the metal-ferroelectric-metal (MFM) capacitors represent low switching cycle endurance, MFM capacitors revealed remnant polarization (Pr) of 70 μC/cm2 and 113 μC/cm2 for RT- and 400 °C-deposited samples, respectively. Ferroelectric films with low-temperature process capability can open a wide range of applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.