Abstract
The influence of the number of solution coatings on the densification of the PZT thick films was studied. PZT powder and PZT precursor solution was prepared by a sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The powder and solution of composition were (A) PZT(80/20)/PZT(20/80), (B) PZT(70/30)/PZT(30/70) and (C) PZT(60/40)/PZT(40/60), (D) PZT(52/48)/PT. The coating and drying procedure was repeated 4 times. And then the PZT precursor solution was spin-coated on the PZT thick films. A concentration of a coating solution was 0.5 moth and the number of coating was repeated from 0 to 6. The porosity of the thick films was decreased with increasing the number of coatings and the PZT thick films with 6-times coated showed the dense microstructure and thickness of about <TEX>$60{\mu}m$</TEX>. A grain size was increased with increasing the coating number. All PZT thick films showed the typical XRD patterns of a typical perovskite polycrystalline structure. The relative dielectric constant of PZT thick films was improved 30-100% as the number of coatings.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Korean Institute of Electrical and Electronic Material Engineers
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.