Abstract
A highly dense and single phase (Ti0.2Zr0.2Hf0.2Mo0.2W0.2)B2 ceramic product is obtained in this work at 1950°C (20 min, 20 MPa) by Spark Plasma Sintering (SPS) from powders prepared by Self-propagating High-temperature Synthesis (SHS). The formation of the (W,Mo)B2 secondary phase is avoided using fine W precursors and adding 1 wt% graphite to the SHS powders before SPS. Kinetic limitations responsible for hindering the synthesis of the high entropy boride are correspondingly eliminated. The resulting 98.5 % dense sample exhibits a homogeneous microstructure, with Vickers hardness of 26.8 GPa. The introduction of 20 vol% SiC produces an increase of the KIC values from 2.32 to 5.11 MPa m1/2. Very relevant is that the volatilization of Mo- and W-oxides occurring during sample oxidation at high temperature, which leads to its rapid degradation with the formation of a very porous oxide scale, can be strongly inhibited by the silicate phases generated in the composite ceramic.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.