Abstract
In the present study, porous TiO2 foams (PTF) were prepared by particle-stabilized emulsion method. The samples having solid contents ranging from 20wt.% to 35wt.% were prepared and successfully impregnated with paraffin without using a surfactant. SEM images showed that the prepared PTFs had three-dimensional interpenetrating structures with good porosities. The pore structure and morphology of PTF was markedly influenced by the solid content. With increase in solid content, porosity decreased, along with a decrease in the homologous encapsulation ratio of paraffin. Differential scanning calorimetry (DSC) evaluated the thermal properties of the paraffin/PTF (PTFP) composites. DSC results showed that with a solid content of 20wt.%, the paraffin adsorption reached 62vol.% and latent heat of the composite PCM was 94.05J/g after 200 melting/freezing cycles. TGA results showed that the form-stable composite PCMs had good thermal stabilities. In order to further enhance the thermal conductivity and improve the adsorption capacity of PTF, sucrose was added to the emulsion and carbonized in situ to form carbon/PTF (PTFC). This could also be successfully impregnated with paraffin to obtain the form-stable composite paraffin/PTFC (PTFCP). The TEM images and results of XPS analysis confirmed that the surfaces of TiO2 particles were covered with a 2nm thick carbon film (C/TiO2). The thermal conductivity of PTFCP increased from 0.302W/mK to 1.059W/mK compared to PTFP, along with a further improvement in adsorption capacity. Furthermore, the results of FT-IR analysis and thermal cyclic tests showed that the form-stable composite PCMs had good chemical stability and thermal reliability after 200melting/freezing cycles. Therefore, the prepared form-stable composite PCMs having excellent pore structures, thermal properties, thermal reliabilities, and chemical stabilities are promising PCM candidates for heat energy storage applications.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.