Abstract
Microstructural evolution during the early stages of ageing (less than one hour) in a Ni–Cr–Fe based superalloy Inconel 718 (IN718) has been investigated using Small-Angle X-ray Scattering (SAXS). The effects of precipitate kinetics on the precipitate size distribution are compared indirectly with SAXS measurements by using Vickers microhardness data. The microhardness increased after 4min of ageing at a temperature of 760°C, although the recorded SAXS data did not reveal the precipitate size distribution. This indicates that the precipitates had not evolved enough to be detected, but still a small number of precipitates increased the yield strength. After ageing the alloy for the shortest period for which data were available, 8min, clear evidence of precipitates could be found from the SAXS data, showing that the γ″- precipitates are about 6nm in width and 3nm in height.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.