The article presents the results of studies of the degree of influence of the operating mode of the centrifugal pump on the intensity of the water jet at constant values of the sediment concentration P = 20 kg/ m3, particle diameter d = 0.25…0.5 mm, test duration T = 2 hours and shaft speed n0 = 2900 rpm. Experiments were carried out on pump feeds from 0.5 Qopt to 1.25 Qopt with various materials and polymer coatings that were applied to the surfaces of the blades made of St.3. The best adhesion of the polymer coating is obtained at a metal temperature of 21°C. Polymer materials based on epoxy resin with silicon carbide have the highest wear resistance, while silumin shows low wear resistance. When testing ground pumps, it was found that parts made of electro corundum on an epoxy-phenol-formaldehyde bond, in comparison with parts made of wear-resistant cast iron, increases the service life of pumps 3 - 8 times.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.