Abstract
In this study, nanocrystalline cellulose (NCC) was used for reinforcement and formaldehyde (HCHO) adsorption of urea-formaldehyde (UF) resin adhesive in fiberboard. The original NCC was modified by 3-aminopropyltriethoxysilane for improving the wetting property with UF resin adhesive. The UF resin adhesive with modified NCC was analyzed by X-ray powder diffraction, thermogravimetric analysis, and Fourier transform infrared. The HCHO emission and bending and bonding strength of the UF resin adhesive with modified NCC were tested according to Chinese National Standard GB/T 17657-1999. Compared with the original UF resin adhesive, modified NCC led to limited effects on the crystal structure, thermal stability, and characteristic absorption peaks of UF resin adhesive. The HCHO emission of the UF resin adhesive with 1.0% modified NCC decreased by 13.0%, while the bending and bonding strength increased by 40.5 and 158.3%, respectively. The improvements of modified UF resin adhesive were destroyed by the reunion of NCC when the content was more than 1.5%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.