Abstract
In this study, nanocrystalline cellulose (NCC) was used for increasing the bonding strength of urea-formaldehyde (UF) resin adhesive, with a reduction of formaldehyde (HCHO) emissions. The surface of NCC was modified by 3-aminpropyltriethoxysilane (APTES) and 3-methacryloxypropyltrimethoxysilane (MPS) for the lack of compatibility with UF resin adhesive. The modified NCC was characterized by X-ray powder diffraction (XRD), thermogravimetric analysis (TG), and wetting property. HCHO emission and bonding strength of the UF resin adhesive with modified NCC were tested according to Chinese National Standards GB/T 17657-1999 and GB/T 9846-2004. The results of XRD, TG, and wetting property from NCC modified by APTES showed more significant improvements than that from NCC modified by MPS. The HCHO emission of UF resin adhesive with 1.5% NCC modified by APTES decreased by 53.2% and bonding strength increased by 23.6%, while the results from the NCC modified by MPS were 21.3% and 7.0%, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.