Abstract
A high- k HfO 2/SiO 2 gate stack is taking the place of SiO 2 as a gate dielectric in field effect transistors. This fact makes the study of the solid-state reaction between these oxides very important. Nanostructure characterization of a high-energy ball milled and post-annealed equimolar HfO 2 and amorphous SiO 2 powder mixture has been carried out by perturbed angular correlations (PAC) technique. The study was complemented with X-ray diffraction and positron annihilation lifetime spectroscopy (PALS). The experimental results revealed that the ball milling of equimolar mixtures increases the defects concentration in hafnium oxide. No solid-state reaction occurred even after 8 h of milling. The formation of HfSiO 4 (hafnon) was observed in the milled blends annealed at high temperatures.The PAC results of the milled samples are compared with those obtained for pure m-ZrO 2 subjected to high-energy ball milling and with reported microstructure data for the system ZrO 2–SiO 2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.