Abstract
The effects of oxygen annealing on the structural properties and leakage current behaviors of sol–gel-derived Bi3.25La0.75Ti3O12-y ferroelectric thin films have been studied. The thin films were pyrolyzed in different atmospheric conditions including a fully oxygenized ambient of 1 bar and an evacuated ambient of less than 10 mbar. X-ray diffraction patterns of the deoxygenated films showed measurable shifts to a higher angle, indicating that each deoxygenated film had a smaller lattice constant than the oxygenated one. Scanning probe analysis showed well-developed grains and inhomogeneous and asymmetric bound charges in both samples. The leakage current behavior of the films was measured as a function of voltage and temperature and was explained on the basis of the Schottky–Simmons thermionic emission model. X-ray photoemission spectra showed that oxygen stability in Bi2O2 layers plays an important role in determining the level of leakage current in the films.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.