Abstract
In this study, magnetic Fe3O4 nanoparticles (NPs) were dispersed uniformly by varying the thickness of the SiO2 coating, and their electronic and magnetic properties were investigated. X-ray diffraction confirmed the structural configuration of monophase inverse-spinel Fe3O4 NPs in nanometer size. Scanning electron microscopy revealed the formation of proper nonporous crystallite particles with a clear core-shell structure with silica on the surface of Fe3O4 NPs. The absorption mechanism studied through the zeta potential indicates that SiO2-coated Fe3O4 nanocomposites (SiO2@Fe3O4 NCs) possess electrostatic interactions to control their agglomeration in stabilizing suspensions by providing a protective shield of amorphous SiO2 on the oxide surface. High-resolution transmission electron microscopy images demonstrate a spherical morphology having an average grain diameter of ∼11-17 nm with increasing thickness of SiO2 coating with the addition of a quantitative presence and proportion of elements determined through elemental mapping and electron energy loss spectroscopy studies. Synchrotron-based element-specific soft X-ray absorption spectroscopy and X-ray magnetic circular dichroism (XMCD) techniques have been involved in the bulk-sensitive total fluorescence yield mode to understand the origin of magnetization in SiO2@Fe3O4 NCs. The magnetization hysteresis of Fe3O4 was determined by XMCD. At room temperature, the magnetic coercivity (Hc) is as high as 1 T, which is about 2 times more than the value of the thin film and about 5 times more pronounced than that of NPs. For noninteracting single-domain NPs with the Hc spread from 1 to 3 T, the Stoner-Wohlfarth model provided an intriguing explanation for the hysteresis curve. These curves determine the different components of Fe oxides present in the samples that derive the remnant magnetization involved in each oxidation state of Fe and clarify which Fe component is responsible for the resultant magnetism and magnetocrystalline anisotropy based on noninteracting single-domain particles.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Langmuir : the ACS journal of surfaces and colloids
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.