Abstract
AlMgB14-TiB2 composite materials were fabricated by self-propagating high-temperature synthesis (SHS) followed by spark plasma sintering of the obtained SHS products. It was found that, during the SHS, the AlMgB14 phase is formed at a donor (Ti + 2B) to acceptor (Al12Mg17-B) mass ratio of 3:7 and 4:6, respectively. The specimen sintered from the SHS powder with the donor:acceptor mass ratio of 5:5 at a temperature of 1470 °C has a uniform skeletal structure. The average hardness of the obtained specimen is 30.1 GPa.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.