Abstract
In this study, 8Cr4Mo4V steel was selected as the research material to develop a numerical model of the macrosegregation phenomenon during vacuum arc remelting (VAR). The accuracy of the model was validated by comparing it with the literature and experimental results. According to the simulation results, molten steel flows down along the solidification front, resulting in positive segregation at the center and negative segregation close to the edge of the ingot. Solute enrichment reduces the undercooling of the alloy system, which in turn decreases the local solidification rate and causes a slight increase in steady-state molten pool depth. Notably, as the molten pool depth increases, the temperature gradient decreases, while the local cooling rate remains nearly constant, which leads to an increase in the local solidification rate again. Consequently, the positive segregation degree at the ingot’s center is gradually alleviated, and the depth of the molten pool gradually decreases. Furthermore, macrosegregation in VAR ingots becomes pronounced with an increase in melt rate. The main reason for this is due to the increased molten pool depth when the melt rate is increasing, which strengthens fluid flow and accelerates the migration of solute elements to the center. Additionally, due to the increase in the extent of solute enrichment when the melt rate is increasing, the degree of fluctuation in both the steady-state molten pool depth and positive segregation increases.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call