Abstract
Mirror electron microscope (MEM) observation has been conducted for a 4-μm-thick n-doped 4H-SiC epitaxial layer. If the sample is simultaneously illuminated with ultraviolet (UV) light of a slightly greater energy than the bandgap energy of 4H-SiC, in-grown stacking faults (IGSFs) can be clearly observed in MEM images. These observations were performed non-destructively, as almost all irradiated electrons returned without impinging the sample surface due to the negative voltage applied to the sample. High spatial resolution observation via MEM showed that multiple IGSFs were stacked up. The phenomenon in which the contrast of the IGSFs vanished in the absence of UV illumination and under UV illumination with a lower energy than the bandgap energy revealed that the origin of the contrast was the negative charging of IGSFs trapping electrons excited by UV light.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.