Abstract
The goal of this study was to compare the shear bond strength (SBS) and failure modes of three different adhesive resins following the use of two different dental curing light units. A total of 160 human premolars were randomly divided into four groups (N = 40 for each): group1, Transbond™ XT (3M Unitek, Monrovia, CA, USA) adhesive paste; group2, Heliosit Orthodontic paste with no primer; group3, Maxcem Elite (Kerr, Orange, CA, USA) self-adhesive resin with prior etching; group4, Maxcem Elite self-adhesive resin with no etching. Each group was further divided into 2subgroups: half (named "a") were cured with VALO LED (Ultradent Products, South Jordan, UT, USA), and the other half (named "b") with the Elipar LED unit (3M Unitek LED, Monrovia, CA, USA). The brackets were submitted to SBS testing 24 h after bonding. Adhesive Remnant Index (ARI) scores and bonding time were also measured. Two-way analysis of variance (ANOVA) and Kruskal-Wallis tests were used for statistical analysis. No significant differences in SBS were observed when comparing the two different LED devices within the same bonding material. The mean SBS of group1 was significantly higher compared to groups2, 3, and 4 (p < 0.001). Mean SBS values of groups2 and 3 were significantly higher than that of group4 (p < 0.001). ARI scores were significantly different in groups4a and 4b compared to the other groups (p < 0.05). Group4a showed significantly lower bonding time/tooth compared to the other groups except to groups3a and 4b (p < 0.001). Decreasing curing time using high-power LED device did not significantly affect SBS. However, the composite type did affect SBS.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of orofacial orthopedics = Fortschritte der Kieferorthopadie : Organ/official journal Deutsche Gesellschaft fur Kieferorthopadie
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.