Abstract
The high wear resistance, high chemical inertness, and high electrical conductivity of magnetron-sputtered transition metal diborides make them a candidate material for sliding electrical contacts. However, their high hardness makes it difficult to penetrate surface oxides, resulting in a high electrical contact resistance. In this study, the authors have investigated how the contact resistance can be improved by the formation of softer Nb-B-C films. The Nb-B-C films were deposited by magnetron sputtering and shown to exhibit a nanocomposite microstructure consisting of nanocrystalline NbB2−x grains with a solid solution of C separated by an amorphous BCx phase. The formation of the BCx phase reduces the hardness from 41 GPa for the NbB2−x film to 19 GPa at 36 at. % C. As a consequence the contact resistance is drastically reduced and the lowest contact resistance of 35 mΩ (contact force 5 N) is achieved for a film containing 30 at. % C. However, crack formation and subsequent delamination and fragmentation is observed for the C-containing Nb-B-C films in tribology tests resulting in high friction values for these films.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Vacuum Science & Technology A: Vacuum, Surfaces, and Films
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.