Abstract
The Nanostructure characteristics of Al3Sc1−xZrx nanoparticles and their effects on the mechanical properties and stress corrosion cracking (SCC) behavior of Al–Zn–Mg alloys were investigated by 3D atom probe analyses, high-angle annular-dark-field scanning transmission electron microscopy methods, electron back scattered diffraction techniques, electrochemical measurements, slow strain rate tests and quantitative calculations. The results show that adding small amounts of scandium (0.10 percent by weight) and zirconium into Al–Zn–Mg extrusion bars can precipitate Al3Sc1−xZrx nanoparticles with a number density of (7.80 ± 3.83) × 1021 per cubic meter. Those particles, with a low lattice misfit with matrix (1.14 ± 0.03 percent) and stable core-shell L12-nanostructure in aged Al–Zn–Mg alloys, can increase the yield strength by 161 ± 7 MPa via strong Orowan strengthening (the theoretical calculated value is 159 MPa) and weak Hall-Petch strengthening (the theoretical calculated value is 6 MPa). Moreover, Al3Sc1−xZrx nanoparticles can change the fracture mechanism of alloys in 3.5% NaCl solution from intergranular cracks to transgranular failure, and decrease the proportion of high-angle grain boundaries from 87% to 31%, thus reducing the microchemistry differences around the grain boundaries and anodic dissolution kinetics, and improving intergranular SCC resistance and ductility. This study offers a new approach to the simultaneous improvement in mechanical property and corrosion performance of high strength alloys.
Highlights
This study offers a new method for the simultaneous improvement in the mechanical properties and stress corrosion cracking (SCC) resistance of high-strength aluminum alloys
We observed that two sets of atomic planes, namely {100} and {010}, perfectly pass through the particles, indicating that Al3 Sc1−x Zrx nanoparticles have full lattice coherency with the matrix (Figure 1b)
The fast Fourier transform (FFT) patterns, taken from the zone axis, revealed that the aluminum matrix and Al3 Sc1−x Zrx both had an ordered of L12 structure (Figure 1c–d)
Summary
The Nanostructure characteristics of Al3 Sc1−x Zrx nanoparticles and their effects on the mechanical properties and stress corrosion cracking (SCC) behavior of Al–Zn–Mg alloys were investigated by 3D atom probe analyses, high-angle annular-dark-field scanning transmission electron microscopy methods, electron back scattered diffraction techniques, electrochemical measurements, slow strain rate tests and quantitative calculations. Al3 Sc1−x Zrx nanoparticles with a number density of (7.80 ± 3.83) × 1021 per cubic meter Those particles, with a low lattice misfit with matrix (1.14 ± 0.03 percent) and stable core-shell L12-nanostructure in aged Al–Zn–Mg alloys, can increase the yield strength by 161 ± 7 MPa via strong Orowan strengthening (the theoretical calculated value is 159 MPa) and weak Hall-Petch strengthening (the theoretical calculated value is 6 MPa). This study offers a new approach to the simultaneous improvement in mechanical property and corrosion performance of high strength alloys.
Sign-in/Register to view highlights & summary Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.