Abstract
Heat treatments at 1300 degrees C, 1400 degrees C, 1500 degrees C, and 1600 degrees C in Ar were found to produce nanoscale precipitates in hot-pressed silicon carbide containing aluminum, boron, and carbon sintering additives (ABC-SiC). The precipitates were studied by transmission electron microscopy (TEM) and nano-probe energy-dispersive X-ray spectroscopy (nEDS). The precipitates were plate-like in shape, with a thickness, length and separation of only a few nanometers, and their size coarsened with increasing annealing temperature, accompanied by reduced number density. The distribution of the precipitates was uniform inside the SiC grains, but depleted zones were observed in the vicinity of the SiC grain boundaries. A coherent orientation relationship between the precipitates and the SiC matrix was found. Combined high-resolution electron microscopy, computer simulation, and nEDS identified an Al4C3-based structure and composition for the nano-precipitates. Most Al ions in SiC lattice exsolved as precipitates during the annealing at 1400 to 1500 degrees C. Formation mechanism and possible influences of the nanoscale precipitates on mechanical properties are discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.