Abstract
Micro-Raman spectroscopy is used to monitor titanium silicide (TiSi <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> ) formation on narrow undoped polycrystalline silicon lines. Linewidths varying from 1.0 μm down to 0.35 μm, with silicidation by rapid thermal anneal (RTA) temperature ranging between 780/spl deg/C and 1020/spl deg/C were analyzed. Phase changes between C49 and C54-TiSi <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> phases were clearly observed. Results demonstrate that analysis of the C54-TiSi <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> Raman peak intensity allowed fast and nondestructive estimation of the process window for low resistivity C54-TiSi <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> formation. Comparison with sheet resistivity measurements showed that micro-Raman scattering provides a complimentary means to electrical analysis for the study of TiSi <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> formation.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call