Abstract
In the present work, 50 vol% Sip/Al–20Si composite was prepared by hot-pressed sintering technology. Si particles were uniformly distributed in the Sip/Al–20Si composite, and only the presence of Si and Al phases were detected by XRD analysis. Dislocations, twins, and stacking faults were found in the Si particles. Several Si phases were found to be precipitated between Al matrix and Si particles. Si/Al interface was clean, smooth, and free from interfacial product. HRTEM indicated that the Si/Al interface was well bonded. The average CTE and thermal conductivity (TC) of Sip/Al–20Si composite were 11.7 × 10−6/°C and 118 W/(m K), respectively. Sip/Al–20Si composite also demonstrated high mechanical properties (bending strength of 386 MPa). Thus, the comprehensive performance (low density and CTE, high TC, and mechanical properties) makes the Sip/Al–20Si composite very attractive for application in electron packaging.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.