Microbridge preparation through spincoating and photolithography without etching

Abstract

It is possible to produce HTSC thin films of polymer metal precursors by the simple spincoating technique. This method can be used to manufacture of Y–Ba–Cu–O- and Bi–Sr–Ca–Cu–O–HTSC thin films. The microbridges are generated into the precursor film by photolithography. The etching process step is cancelled. After that the superconducting phases are formed at 950°C respectively 865°C during the tempering process. The HTSC structures serve as a previous stage for SNS contact. The critical temperatures ( T c ) measured on the 20 and 200 μ m wide microbridges are 82 K for Y–Ba–Cu–O and 108 K for Bi–Sr–Ca–Cu–O. The critical current density ( j c ) obtained is 10 5 A/cm 2 for 65 K.