Abstract
Thick a-C/a-C:Ti multilayer films with bilayer periods of 12–70nm were deposited on Ti6Al4V alloy substrate by means of closed field unbalance magnetron sputtering. The morphology and microstructure of the multilayer films were investigated by scanning electron microscopy, high resolution transmission electron microscopy and X-ray photoelectron spectroscopy. Nanocrystalline TiC was distributed in the a-C:Ti layer and at the interface between the two adjacent layers. The mechanical and tribological properties were evaluated by Rockwell and scratch tests, a nanoindentor and a ball-on-disk tribometer. The multilayer film with a bilayer period of 12nm showed the highest adhesion strength, hardness (26GPa) and elastic modulus (232GPa); it also had the lowest average coefficient of friction (0.09) and a wear rate of 8.06×10−17m3N−1m−1.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.