The structural-phase composition and tribological and performance properties of coatings based on an 86WC-10Co-4Cr composition obtained by the HVOF method at varying (150 L/min, 170 L/min, 190 L/min) oxygen flow rates were studied. The results showed that the coefficient of friction of coatings in gear oil remained almost unchanged with the variation in oxygen flow rate. However, microhardness increased significantly with an increasing oxygen flow rate, reaching a maximum at 190 L/min. An increasing oxygen flow rate was also accompanied by an increase in roughness and coating thickness, with a decrease in porosity, particularly notable at 190 L/min. Adhesion strength reached the maximum values for the A2 and A3 coatings under high loads. The phase composition of the coatings included WC, W2C and CoO phases irrespective of the oxygen flow rate, and their microstructure was characterized by a more homogeneous and dense structure. Thus, this study confirmed that the optimal oxygen flow rate for achieving an improved performance and tribological characteristics of 86WC-10Co-4Cr coatings is 190 L/min.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.