Investigation of Flux-Line Assembly Mechanical Properties in 2223-Phase Bi(Pb)SrCaCuO Ceramic by Magneto-Mechanical Measurements

Abstract

Measurements are performed of dissipation and apparent modulus change of the flux-line assembly in a 2223 phase pure ceramic specimen of Bi(Pb)SrCaCuO. Two dissipation peaks arc observed; the amplitude dependence of the low temperature peak confirms a thermally activated depinning picture, while the behaviour of the high-temperature peak is in evident contrast to such a model. The characteristics of the second peak, as well as the extension of the magnetization transition over 50 K below Tc are in favour of a complex cooperative transition of the mixed state, controlled by the weak links between grains. Dissipationsmessungen und Messungen der auftretenden Modulanderung dcr Fluslinienanordnung in einer reinen (2223)-Phasen-Keramikprobe von Bi(Pb)SrCaCuO werden durchgefuhrt. Zwei Dissipationsmaxima werden beobachtet; die Amplitudenabhangigkeit des Niedertemperaturmaximums bestatigt ein thermisch aktiviertes Entankerungsverhalten, wahrend das Verhalten des Hochtcmperatur-maximums im augenscheinlichen Kontrast zu einem derartigen Modell steht. Sowohl die Charakteristiken des zweiten Maximums als auch die Ausdehnun des Magnetisierungsubergangs uber 50 K untcrhalb Tc weisen auf einen komplexen, kooperativen Ubergang des Mischzustands hin, der von den schwachen Verknupfungen zwischen den Korncrn gesteuert wird.