Interface chemistry of CdZnTe films studied by a peel-off approach

Abstract

CdZnTe films with thickness above 50μm were deposited at temperatures of 200–500°C by Close Space Sublimation method. A peel-off approach has been adopted to study the interface chemistry of CdZnTe thick films. For all the CdZnTe films, the scanning electron microscopy images show the small and round-like grains formed at interface in contrast to the large ordered grains at surface. For CdZnTe films grown at a low substrate temperature of 200°C, the interface layer between CdZnTe and substrate is mixed with Te and CdTe, as evidenced by X-ray diffraction, Raman and X-ray photoelectron spectroscopy results. The thickness of the interface layer can be estimated to be 84nm by depth profile using X-ray photoelectron spectroscopy. In contrast, a thin interface layer less than 14nm is found at a high substrate temperature of 500°C. The limited reaction of Te2 and Cd (Zn) to CdZnTe at a low growth temperature is responsible for the formation of the thick interface layer and a slow deposition rate at the nucleation stage.