Abstract
InGaN multiple quantum well (MQW) laser diodes were fabricated on (0001)Si oriented 6H–SiC substrate using low-pressure metal organic vapor phase epitaxy (LP-MOVPE). The laser oscillation was observed above the threshold current of 800 mA at a peak wavelength of 414.3 nm under pulsed current injection at room-temperature. The pulse duration was 300 ns and the repetition frequency was 1 kHz. The threshold current density and differential efficiency were estimated to be 16 kA/cm2 and 0.03 W/A, respectively. The full width at half maximum (FWHM) of the lasing emission lines was between 0.03 nm and 0.21 nm. Streak-shaped far field patterns were clearly observable. The lifetime of the laser diode was more than 5 hours.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.