Abstract
Magnetic photocatalytic Fe3O4@TiO2 composites have been fabricated by changing the concentration of (NH2)2CO. Samples were named as low (NH2)2CO concentration group which the (NH2)2CO concentration in the synthesis process was below 2.25 mol/L and high (NH2)2CO concentration group which the (NH2)2CO concentration was above 2.5 mol/L. Photocatalytic degradation experiments of methyl orange showed that the final degradation rates of low (NH2)2CO concentration group samples were higher than that of high (NH2)2CO concentration group, even better than P25 at the same test conditions. And it was interesting that samples of low (NH2)2CO concentration group had smaller values of BET surface areas than that of high (NH2)2CO concentration group. It indicated that the improvement of photocatalytic activity which was effected by BET surface areas was not obvious. There were two main factors enhancing the photocatalytic property of low (NH2)2CO concentration group: First, diffusing reflection spectra showed that the low (NH2)2CO concentration group samples had lower reflectivity, this suggested that the structure improved the efficiency of light absorption; Second, NH4+ would take up the active sites on the surface of the TiO2 particles, the FT-IR test results showed that the samples of the low (NH2)2CO concentration group samples bonded less NH4+, thus leading to the higher photocatalytic activity. It had enlightenment role for optimizing the performance of photocatalytic materials.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.