Abstract
In this study, the effect of heat treatment on the mechanical and microstructural properties of welded joints after friction stir welding of age-hardenable Al-Zn-Mg-Si-Cu wrought aluminum alloy plates was investigated. For this purpose, some of the samples welded using FSW technique with a rotational speed of 1250 rpm and a traverse speed of 40 mm·min-1 were subjected to annealing and some to artificial aging heat treatment at different temperatures and times. In FSWed artificial aged samples where AlFeSi precipitate formations were detected, hardness and strength increase were realized with grain-boundary strengthening and Orowan hardening mechanisms. The lowest ultimate tensile strength was 156.3 N·mm-2 in the annealed sample, while the highest ultimate tensile strength was 210.8 N·mm-2 in the sample artificially aged at 190 °C for 2 hours. Fractographic examination revealed that ductile fracture occurred in all specimens.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Similar Papers
More From: International Advanced Researches and Engineering Journal
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.