Abstract
Backup rolls are the main tool in a four-high rolling mill; the rolling forces applied in load cells promote the fatigue of the material due to mechanical contact between backup rolls and work rolls. This work investigated the causes of recurrent failures in backup rolls, with cracking always initiated on the surface of the roll body and finishing in the main radius between neck and roll body. Aiming to find the causes of failure, visual inspection and morphology of the fracture were performed, complemented with mechanical tests of hardness on the stress concentration area, in addition to validating the results by applying the finite element method, using ANSYS Mechanical Static Structural Software. It was concluded that the fatigue crack initiated on the surface of BUR due to work hardening continued growing up over the fatigued material, creating beach marks, and finally, a fracture occurred in the main radius of BUR due to stress concentration. The work hardening is the main cause of spalling on BURs and other mechanical components exposed to mechanical contact.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.