Abstract
A Mn-enriched Ni46.4Mn32.8Sn20.8 Heusler alloy has been prepared by the induction melting and casting method. The samples used were annealed at 900°C during 72 h with a subsequent water quench. The magnetostructural transformation (MST) in the vicinity of Tm=230K and Ta=250K has been found, and characterized by DSC, magnetization and resistivity measurements. Changes in the crystal structure due to the MST were observed using neutron diffraction at different temperatures. The crystal structure of martensitic phase shows a good fits to the 4-layered orthorhombic martensite with a Pmma space group. The linear shift of transformation temperatures was found in the entire high magnetic field range up 14T to be dTm/dB0 = -1.50 K/T and dTa/dB0 = -1.26 K/T, whereas in the low field range we found an increase of both characteristic temperatures. The entropy changes at the MST were evaluated using the Clausius-Clapeyron relationship. The transformation-induced magnetoresistance has been measured.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.