In situ powder synchrotron and neutron diffraction study of Zr 2Ni deuterides

Abstract

Zr 2Ni (tetragonal, Al 2Cu-type structure) absorbs deuterium up to the composition Zr 2NiD 4.8. The crystal structure of Zr 2Ni deuterides were investigated at ambient and elevated temperatures. Synchrotron radiation powder X-ray diffraction (SR-PXD) reveals a triclinic distortion of Zr 2NiD 4.8 at room temperature; a = 6.81744(8) Å, b = 6.80177(8) Å, c = 5.69042(4) Å, α = 90.191(1)°, β = 90.200(1)°, γ = 90.2886(8)°, space group P 1 ¯ . On heating to 473 K in a closed, small-volume capillary, the metal sublattice of the deuteride returns to tetragonal symmetry with a modest loss of deuterium. Powder neutron diffraction (PND) shows that the saturated deuteride takes a superstructure at room temperature. On heating under isobaric conditions (1 bar D 2) the ordering gradually vanishes and the deuterium content is reduced considerably. PND data recorded at 373, 473 and 573 K can be adequately fitted with simple tetragonal unit cells although remnants of ordering peaks are present up to 473 K. Four crystallographically different sites in the tetragonal structure were found to be occupied by deuterium. The site preference is mainly dependent on sample composition and to a lesser extent on the temperature. Decomposition starts at 723 K. The sample is completely decomposed into tetragonal ZrD 2 and Zr 7Ni 10 at 873 K.