Abstract

High quality Sr0.8La0.067Ti0.8Nb0.2O3-δ ceramics containing inclusions of Cu or Fe were prepared by the mixed oxide route and sintered under reducing conditions at 1700 K. Products were high density; Fe enhanced density (to 98% theoretical) and grain size (to 15 μm) whilst Cu tended to reduce both slightly. XRD and SEM analyses showed that the material is mainly composed of cubic SrTiO3 phase, with rutile-structured minor phases and metallic inclusions along the grain boundaries. The inclusions increased carrier concentration and carrier mobility, leading to a reduction in electrical resistivity by a factor of 5 and increase in power factor by 75%. Both types of metallic inclusions were beneficial, increasing the thermoelectric figure of merit (ZT) from 0.25 at 1000 K for the control sample, to ZT of 0.36 at 900 K for the Cu-containing samples and to 0.38 at 1000 K for the Fe-containing samples.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.