Abstract
AbstractIn this paper the impact of post deposition annealing in various ambient on electrical properties of hafnium zirconate (HfxZr1-xO2) high-k dielectrics is reported. ALD HfxZr1-xO2 films are annealed in a nitrogen and/or oxygen ambient at 500°C to 1000°C. Devices annealed at 500°C in N2 has lower equivalent oxide thickness (EOT) of 10Å without significant increase in gate leakage (Jg), threshold voltage (Vt) and only a slight decrease in transconductance (Gm) values compared to 500°C O2 annealed devices. Furthermore, the impact of annealing HfxZr1-xO2 films in a reducing ambient (NH3) is studied. Optimized NH3 anneal on HfxZr1-xO2 results in lower CET, improved PBTI, low sub-threshold swing values, comparable high-field Gm with only a minor degradation in peak Gm compared to control HfxZr1-xO2. Finally, the impact of laser annealing vs. RTP annealed HfxZr1-xO2 films are reported. Laser annealing helped further stabilize tetragonal phase of HfxZr1-xO2 without inducing void formation. Good devices with low leakage, low EOT and high mobility are obtained for laser annealed HfxZr1-xO2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.