Abstract

In this paper, we used micro-Raman spectroscopy in cross-section to investigate the effect of different doping on the distribution of stress in the silicon substrate and the grown 3C-SiC film. The 3C-SiC films with a thickness up to 10 μm were grown on Si (100) substrates in a horizontal hot-wall chemical vapor deposition (CVD) reactor. To quantify the influence of doping on the stress distribution, samples were non-intentionally doped (NID, dopant incorporation below 1016 cm-3), strongly n-type doped ([N] > 1019 cm-3), or strongly p-type doped ([Al] > 1019 cm-3). Sample NID was also grown on Si (111). In silicon (100), we observed that the stress at the interface is always compressive. In 3C-SiC, instead, we observed that the stress at the interface is always tensile and remains so in the first 4 µm. In the remaining 6 µm, the type of stress varies according to the doping. In particular, for 10 μm thick samples, the presence of an n-doped layer at the interface maximizes the stress in the silicon (~700 MPa) and in the 3C-SiC film (~250 MPa). In the presence of films grown on Si(111), 3C-SiC shows a compressive stress at the interface and then immediately becomes tensile following an oscillating trend with an average value of 412 MPa.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.