Abstract
This research was conducted to study the form of corrosion products of medium carbon steel under the exposure of Banda Aceh’s atmosphere. The medium carbon steel samples which the size based on ASTM G 50 were exposed in open areas around the Engineering Faculty, Syiah Kuala University, Darussalam - Banda Aceh, Aceh province, Indonesia. The study was carried out from January through December 2016. The corrosion product formed on the surface of the samples was studied using X-ray Diffraction (XRD) and Scanning Electron Microscope (SEM) method. Measurements of weight loss due to atmospheric corrosion as a basis for calculating corrosion rates was referring to ASTM G1. Corrosion product found based on XRD analysis was lepidocrocite (FeO2, γ-FeOOH) and goethite (FeO2, α-FeOOH). The results agreed with SEM analysis that also indicates to lepidocrocite and goethite. The corrosion rate for twelve months showed that the highest rate occurs in the period of March-April that was 0.024 mpy. During twelve months exposure, the corrosion products consist of lepidocrocite and goethite. Significant changes began to occur in the eighth month, where the product of corrosion was almost entirely goethite.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.