Abstract
Four different commercial coatings, TiN, Cr, CrN, and Cr/CrN (multilayer) were deposited by physical vapor deposition (PVD) on high resistivity chemical vapor deposited (CVD) SiC for the dual purpose of corrosion mitigation and fission gas hermeticity. The coatings were exposed for up to 2600 hours in flowing high temperature (288-350°C), high purity, liquid water with dissolved hydrogen (0.15-3ppm) or dissolved oxygen (1-2ppm). The Cr/CrN coatings did not adhere well and spalled quickly during exposure. In oxygenated conditions, none of the coatings were protective . CrN coatings spalled preferentially at defect sites, but reacted slowly enough in the absence of defects to potentially be chemically protective. TiN coatings fully oxidized within a few hundred hours and spalled. In hydrogen, all the coatings were chemically stable. Coating failures were identified and attributed to localized spallation, potentially related to coating defects. Coating improvements are recommended to reduce spallation and improve coating protection for future generations of dual-purpose coatings.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.