Abstract
Hydrogen absorption of biomedical titanium and Ni-Ti alloys in a neutral fluoride (2.0% NaF) solution for up to 10,000 h at 37 degrees C has been evaluated by means of hydrogen thermal desorption analysis. For alpha titanium (commercial pure titanium), the amount of absorbed hydrogen was, at most, 10-30 mass ppm, and the corrosion product and hydride formation were revealed on the surface of the specimen by X-ray diffraction analysis. Ni-Ti superelastic alloy absorbed approximately 150 mass ppm of hydrogen, which was probably sufficient to result in the pronounced degradation of the mechanical properties, although corrosion was hardly observed. In contrast, hydrogen absorption of alpha-beta titanium (Ti-6Al-4V) and beta titanium (Ti-11.3Mo-6.6Zr-4.3Sn) alloys was negligible, although general corrosion was observed. The results of the present study indicate that the susceptibility of titanium and Ni-Ti alloys to hydrogen absorption in the neutral fluoride solution is different from that in the acidic fluoride solution reported previously.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Biomedical Materials Research Part B: Applied Biomaterials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.